Solder Paste SP15TSC

Lead free soldering pastes designed for solde-

ring SMD electronic components. The soldered

connections are characterised by good electrical

and mechanical parameters. The paste composition

eliminates the effect of lifting SMD components during

soldering. The paste is available in 10ml/25g syringe.

Flux Type: T Y P 1.1.2.C

Alloy: Sn95,5Ag3,8Cu0,7

Solder Bar LZ 1000

For solder bath

Suitable for dip, selective and wave soldering

4 x cca 250g

Flux Type: F-SW32

Alloy: Sn99Cu1

Flux Content: 0%

Melting Temperature: 227°C

Part No. Ord.No. Description

LZ1000TC Sn99Cu1 53078 1kg

Part No. Ord.No. Description

SP15TSC-10 Sn95,5Ag3,8Cu0,7 56741 10ml

Lead solders

AS Series

Fluitin AS is an activated rosin cored solder wire develo-

ped for general hand soldering applications where halide

free flux has been specified.

Flux Type: F-SW32

Alloying: Sn60Pb38Cu2

Flux Content: 1,5% (0,5mm) / 3,5% (1mm)

Melting Temperature: +18 3°C to +190°C

1532 Series

Activated rosin cored solder wire developed for general

hand soldering applications. The unique activator system

offers good thermal stability at pre-soldering temperatu-

res ensuring that Fluitin 1532 performs extremely well

on parts and surfaces which present poor or difficult

soldering conditions. Fluitin 1532 leaves post-soldering

residues that are hard and which can be safely left without

the need to remove them.

Flux Type: F-SW26

Alloying: Sn60Pb38Cu2

Flux Content: 2,2%

Melting Temperature: +18 3°C to +190°C

2630 Series

This solder wire is used for applications requiring

a higher activity, for components with poor sol-

derability, especially for soldering operations on

transformers, soldering on cooper cables with large dia-

meters, where a stronger flux is needed to cope with a hig

thermal capacity of the components to be soldered. It is

also used for soldering ofn nickel surfaces, critical com-

ponents and robotic soldering with short cycle times.

Flux Type: T Y P 1.1.2

Alloy: Sn60Pb38Cu2

Flux Content: 2,2%

Melting Temperature: +18 3°C to +190°C

Part No. Ord.No. Description

1532 Sn60Pb38Cu2 12701 0,75mm 1kg 2,2%

1532 Sn60Pb38Cu2 53080 0,75mm 250g 2,2%

1532 Sn60Pb38Cu2 12702 1mm 250 g 2,2%

1532 Sn60Pb38Cu2 12704 1mm 1kg 2,2%

1532 Sn60Pb38Cu2 12708 1,5mm 1kg 2,2%

1532 Sn60Pb38Cu2 41360 1,5mm 10g 2,2%

Part No. Ord.No. Description

AS Sn60Pb38Cu2 53521 0,5mm 250g 1,5%

AS Sn60Pb38Cu2 6581 1mm 1kg 3,3%

Part No. Ord.No. Description

2630 Sn60Pb38Cu2 56978 0,7mm 250g

2630 Sn60Pb38Cu2 53075 1mm 1kg

HS10 Series

is very efficient by its high activity, which results

in quick spread of solder and electrical safe

residues.

Halide activated rosin flux Can be used for hand and

robot soldering

Flux Type: T Y P 1.1.2

Alloy: Sn60Pb40

Flux Content: 2,5%

Melting Temperature: +18 3°C to +190°C

HF32 Series

HF-32 is a no-clean flux cored solder wire. The

activated, halide-free flux meets DIN EN 29454

Typ 1.1.3 standard. HF-32 can be used for hand-

soldering and automatic wire feed operations. For manual

soldering, the soldering iron tips should be temperature-

controlled, to prevent excessive heat from being applied

to the wire. Flux spatter from the formulation is minimal.

Flux Type: T Y P 1.1.3

Alloy: Sn60Pb38Cu2

Flux Content: 3,5%

Melting Temperature: +18 3°C to +190°C

LC60M2 Series

Sn60Pb38 solder manufactured in the first

melt of tin and lead according to PN EN

29453:2000 standard in continuous casting process

in air-free environment; afterwards extruded, in order to

eliminate oxide occurrence.

Flux Type: T Y P 1.1.3

Alloying: Sn60Pb38Cu2

Flux Content: 2,2%

Melting Temperature: +18 3°C to +190°C

Part No. Ord.No. Description

HS10 Sn60Pb40 41122 0,7mm 250g

HS10 Sn60Pb40 24165 0,7mm 1kg

HS10 Sn60Pb40 24756 1mm 250g

HS10 Sn60Pb40 75093 1mm 500g

HS10 Sn60Pb40 53074 1mm 1kg

Part No. Ord.No. Description

HF32 Sn60Pb38Cu2 53076 1mm 250g

HF32SMD Series

No-clean flux, can be used for hand-soldering

and automatic wire feed operations.

• low flux content

• reduced rosin content

• high organic acid content - appropriate to SMT applica-

tions

• halide free

Flux Type: T Y P 1.1.3B

Alloy: Sn60Pb40

Flux Content: 1%

Melting Temperature: +18 3°C to +190°C

Part No. Ord.No. Description

HF32SMD Sn60Pb40 53077 0,5mm 100g

Part No. Ord.No. Description

LC60M2 Sn60Pb38Cu2 57183 1mm 1kg

Triangular Stick Solder

Alpha Cleanwave 63/37 is manufactured using only high

purity metals in its formulaion together with proprietary

dross reducing technology.

Creating low oxide formation and excellent wetting.

4x cca 250g

Flux Type: F-SW32

Alloying: Sn63Pb37P

Flux Content: 0%

Melting Temperature: +18 3°C

Part No. Ord.No. Description

CLEANWAVE 51700 Sn63Pb37P 1757 1 kg

Triangular Stick Solder

For solder bath

Suitable for dip, wave and selecting soldering

Flux Type: F-SW32

Alloying: Sn63Pb37

Flux Content: 0%

Melting Temperature: +18 3°C

Part No. Ord.No. Description

EL250E37 Sn63Pb37 70111 1 pc (cca 250g)

L 18

Soldering Equipment

www.soselectronic.com • inf[email protected] • DE: +49 (0) 8151 44 97 11 • : +421 55 786 04 19

Solders

1 2 ... 14 15 16 17 18 19 20

Comentarios a estos manuales

Sin comentarios

AIT iTool Manual de usuario Pagina 19

Comentarios a estos manuales

Relacionado con productos y manuales para Grabadores de vídeo digital (dvr) AIT iTool